Izitovu zokufudumeza zizixhobo ezibalulekileyo kumashishini afana ne-metallurgy, ubunjineli beekhemikhali, kunye nokuveliswa kombane, kwaye ukusebenza kwazo okuzinzileyo kuxhomekeke kakhulu kwizitena ezirhabaxa ezikumgangatho ophezulu. Ukukhethwa kwezitena ezirhabaxa kuxhomekeke kubushushu bokusebenza kwesitovu, umthwalo wobushushu, imeko-bume yeekhemikhali, kunye neemfuno zesakhiwo. Apha ngezantsi kukho intshayelelo eneenkcukacha kwizitena ezirhabaxa ezisetyenziswa kakhulu kwizitovu zokufudumeza, ezikunceda ukhethe isisombululo esifanelekileyo kwiimfuno zakho zoshishino.
Izitena ze-Fireclay
Izitena zodongwe lomlilo zezona zitena zisetyenziswa kakhulu kwizitovu zokufudumeza. Zenziwe nge-kaolin ezimalungaI-30% Al₂O₃, zinokumelana kakuhle nobushushu kwaye zixabisa kancinci, nto leyo ezenza zilungele iindawo ezinobushushu obuphakathi.(1200–1400℃)njengeendonga ze-oven, ii-flue, kunye nee-top ze-oven ezishushu kancinci. Uzinzo lwazo oluhle kubushushu luthintela ukuqhekeka kotshintsho olukhawulezileyo lobushushu, ngelixa ukufikeleleka kwazo kunceda ukulawula iindleko zeprojekthi iyonke, nto leyo eyenza zibe lukhetho olungabizi kakhulu kwii-oven eziqhelekileyo zoshishino.
Izitena ze-Alumina eziphezulu
Izitena ze-alumina eziphezulu ziyindlela ephuculweyo yokukhetha izitena ezifakwe udongwe lomlilo, eziquka ngaphezuluI-48% Al₂O₃Ngokungaguquguquki okuphezulu(1400–1600℃), amandla angcono okucinezelwa, kunye nokumelana nokukhukuliseka okunamandla, zifanelekile kwiindawo ezinobushushu obuphezulu ezifana nee-linings ze-furnace, ii-top ze-furnace, kunye neengcango ze-furnace. Zihlelwe ngokomxholo we-Al₂O₃, ziyahlangabezana neemfuno zobushushu ezahlukeneyo, nto leyo ezenza zisetyenziswe kakhulu kwii-furnace zokufudumeza ze-metallurgical kunye neekhemikhali apho kufuneka uzinzo lobushushu obuphezulu.
Izitena zeSilica
Izitena zeSilica, kunyeUmxholo weSiO₂ ongaphezulu kwe-94%, i-excel kwizinga lobushushu obuphezulu, kunye nobushushu bokuthambisa umthwalo obungaphezulu1650℃Zisetyenziswa kakhulu kwiindawo ezinobushushu obuphezulu kakhulu ezifana nee-oven tops kunye ne-regenerators, ingakumbi kwiindawo ezishushu ezikhupha i-oxidizing. Nangona kunjalo, ukumelana kwazo nobushushu obuphantsi kuyawuthintela ukusetyenziswa kwazo kwiindawo ezinokuguquguquka rhoqo kobushushu.
Izitena ezivuselela i-alkaline
Izitena ezichasene ne-alkaline, kuquka izitena ze-magnesia kunye nezitena ze-magnesia-alumina, zenzelwe iimeko ezinzima.I-MgO, ingamelana namaqondo obushushu afikelela kwi2000℃kwaye zinokumelana okukhulu ne-alkaline slag, nto leyo ezenza zifaneleke kwiibhothi zesithando somlilo kunye nemigca ye-slag xa zidibene ne-alkaline melts. Izitena zeMagnesia-alumina ziphucula ukumelana nobushushu ngokongeza i-alumina, zilungele iimeko zokusebenza ezinzima ngakumbi.
Izitena ezikhethekileyo ezirhabaxa
Izitena ezikhethekileyo ezichaseneyo nezitena ze-corundum(Al₂O₃ ≥90%)kwaye izitena ze-silicon carbide zisetyenziselwa izinto ezibalulekileyo. Izitena ze-Corundum ziyamelana namaqondo obushushu angaphezulu1800℃kwaye zilungele iindawo ezichatshazelwe ngqo ngamalangatye okanye ukukhukuliseka okukhulu kwenkunkuma. Izitena ze-silicon carbide zibonelela ngokumelana nokuguguleka okugqwesileyo kunye nokumelana nokutshayiswa bubushushu, zifanelekile kwiibhothi zesithando somlilo, iiflue, kunye nezinye iindawo eziguguleka kakhulu.